| Resistivity－temperature characteristics of sol gel YBa2Cu3Oy samples synthesized in flowing oxygen atmosphere |
| |
| 引用本文： | 周增均,周卓为,周良玉,林莉,李星国,冯庆荣.Resistivity－temperature characteristics of sol gel YBa2Cu3Oy samples synthesized in flowing oxygen atmosphere[J].中国物理 B,2004,13(11):1957-1961. |
| |
| 作者姓名： | 周增均 周卓为 周良玉 林莉 李星国 冯庆荣 |
| |
| 作者单位： | School of Physics and State Key Laboratory of Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871, China;School of Physics and State Key Laboratory of Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871, China;School of Physics and State Key Laboratory of Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871, China;Department of Chemistry, Peking University, Beijing 100871, China;Department of Chemistry, Peking University, Beijing 100871, China;School of Physics and State Key Laboratory of Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871, China |
| |
| 基金项目： | Project supported by China National Centre for Research and Development of Superconductivity (Grant No BKBRSF G1999064602). |
| |
| 摘 要： | The relationship of resistivity versus synthesizing temperature of sol gel YBa_2Cu_3O_y samples was studied when prepared under flowing oxygen conditions. A set of high-temperature ρ－T curves was obtained for the whole process. After the sample finished the test measuring, its resistivity was ρ_{300}=9.83×10^{-3 }Ω·cm at room temperature. The ρ－T curve also showed that the orthorhombic－tetragonal phase transformation of sol-gel YBa_2Cu_3O_y sample occurred at 581℃ for the sample in the rising temperature process, but at 613℃ in the cooling process, lower than that of the samples made by using the conventional powder metallurgy methods.
|
| 关 键 词： | sol gel YBa_2Cu_3O_y sample ρ－T curve resistivity phase transformation |
| 收稿时间： | 2004-04-27 |
Resistivity－temperature characteristics of sol gel YBa2Cu3Oy samples synthesized in flowing oxygen atmosphere |
| |
| Zhou Zeng-Jun,Zhou Zuo-Wei,Zhou Liang-Yu,Lin Li,Li Xing-Guo and Feng Qing-Rong.Resistivity－temperature characteristics of sol gel YBa2Cu3Oy samples synthesized in flowing oxygen atmosphere[J].Chinese Physics B,2004,13(11):1957-1961. |
| |
| Authors: | Zhou Zeng-Jun Zhou Zuo-Wei Zhou Liang-Yu Lin Li Li Xing-Guo and Feng Qing-Rong |
| |
| Institution: | Department of Chemistry, Peking University, Beijing 100871, China; School of Physics and State Key Laboratory of Artificial Microstructure and Mesoscopic Physics, Peking University, Beijing 100871, China |
| |
| Abstract: | The relationship of resistivity versus synthesizing temperature of sol gel YBa_2Cu_3O_y samples was studied when prepared under flowing oxygen conditions. A set of high-temperature ρ－T curves was obtained for the whole process. After the sample finished the test measuring, its resistivity was ρ_{300}=9.83×10^{-3 }Ω·cm at room temperature. The ρ－T curve also showed that the orthorhombic－tetragonal phase transformation of sol-gel YBa_2Cu_3O_y sample occurred at 581℃ for the sample in the rising temperature process, but at 613℃ in the cooling process, lower than that of the samples made by using the conventional powder metallurgy methods. |
| |
| Keywords: | sol gel YBa_2Cu_3O_y sample ρ－T curve resistivity phase transformation |
|