Specific volume studies of γ-irradiated polytetrafluoroethylene from 40 to 150°C

The effect of γ-irradiation and post-irradiation heat treatment on the specific volume versus temperature relationships of polytetrafluoroethylene (PTFE) samples (1/2-in. diameter rods) have been studied over the 40–150°C. temperature range for radiation doses up to 8.9 X 10⁸ rad. At low doses the specific volume at any temperature decreased with dose, but above about 10⁸ rad it increased with dose. Similarly, the rate of volumetric expansion initially decreased with dose, while, at very high doses (8.9 X 10⁸ rad) the rate of expansion at temperatures above 100°C. exceeded that of the unirradiated PTFE. Heating at 150°C. for 100 hr. produced a substantial decrease in the specific volume and a decrease in the rate of expansion for the irradiated samples. Irradiation effects in PTFE are considered to be a result of such factors as radiation-induced chain scission, increased crystallinity, and increased void content. Changes resulting from post-irradiation heat treatment can be attributed to increased crystallinity, decreased void content, and weight loss.