A facile green approach to the synthesis of Bi2WO6@V2O5 heterostructure and their photocatalytic activity evaluation under visible light irradiation for RhB dye removal

Bismuth tungsten oxide and vanadium pentoxide (Bi₂WO₆/V₂O₅) heterostructures are produced by a green synthesis approach using Azadirachta indica extract for photocatalytic performance. The hydrothermal method at temperatures between 120 °C and 140 °C is used to synthesize Bi₂WO₆. Bi₂WO₆ and V₂O₅ phases are formed in pure orthorhombic wells according to the XRD pattern. The SEM displays V₂O₅ nanorods, Bi₂WO₆ hierarchical microspheres that resemble flowers at 120 °C, and particles with a particle-like character at 140 °C. In V₂O₅, the asymmetric stretching vibrations of the triplely coordinated oxygen (chain oxygen) bonds and the vibration of the doubly coordinated oxygen (bridge oxygen) bonds are responsible for a peak at 611 cm^?1. In FTIR spectra between 600 and 1600 cm^?1, the major absorption bands in Bi₂WO₆ are attributed to the W-O stretching, Bi-O stretching, and W-O-W bridging stretching modes. Bi₂WO₆@V₂O₅ at 120 °C has the lowest bandgap energy (2.32 eV) and optical electronegativity (0.62), as well as the highest refractive index (2.57), extinction coefficient (2.21), and dielectric constant (ε_r = 0.72 and ε_i = 11.4) among all samples, making it a suitable material for photocatalysis. Rhodamine blue (RhB) dye degradation is used to measure the photocatalytic activity (PCA) of certain materials. The results showed that heterostructure V₂O₅@Bi₂WO₆ synthesized at 120 °C is more attractive among all samples due to high degradation of RhB dye under sunlight irradiation in 90 min.