Effect of syndiotacticity on the aqueous poly(vinyl alcohol) gel 2. Syneresis of gel

Summary The mechanism of syneresis of an aqueous gel of syndiotacticity-rich poly(vinyl alcohol) (PVA) with the rise of temperature was studied using the PVA having the content of syndiotacticity in diad from 58.4 to 66.2%. The extent of syneresis was estimated by gravimetry. Syneresis of gel with the rise of temperature depends upon the syndiotacticity and gelling temperature. The gel chilled at lower temperature of PVA having the content of syndiotacticity in diad above 60.9% showed remarkable syneresis with the rise of temperature. The maximum of the extent of syneresis appeared between the content of syndiotacticity in diad of 60.9% and that of 64.2%. The phenomena of syneresis was not thermally reversible. Syneresis occurs accompanying the breakdown of the unstable junction and further growth of the crystallite.

---

Zusammenfassung Der Mechanismus der Synärese an wäßrigen Gelen von Polyvinylalkohol, reich an syndiotaktischem Anteil, wurde mit steigender Temperatur untersucht, wobei der Polyvinylalkohol in Bezug auf seinen Gehalt an syndiotaktischen Diaden zwischen 58,4 und 66,2% variiert. Die Synärese wurde gewichtsmäßig verfolgt. Die Synärese hängt von der Syndiotaktizität und der Gelierungstemperatur ab. Gele, erstarrt bei tieferen Temperaturen mit einer Syndiotaktizität von 60,9%, zeigten beträchtliche Synärese mit steigender Temperatur. Das Maximum an Synärese wurde zwischen 60,9 und 64,2% Syndiotaktizität beobachtet. Das Phänomen der Synärese ist nicht thermisch reversibel. Die Synärese läuft ab unter Zusammenbruch von unstabilen Bindungen und weiterem Wachstum der Kristallite.

---

---

Part 1. cf. reference 4.