Effect of interfacial diffusion on microstructure and properties of FePt/B4C multifunctional multilayer composite films

FePt/B₄C multilayer composite films were prepared by magnetron sputtering and subsequent annealing in vacuum. By changing Fe layer thickness of [Fe/Pt]₆/B₄C films, optimal magnetic property (8.8 kOe and remanence squareness is about 1.0) is got in [Fe(5.25 nm)/Pt(3.75 nm)]₆/B₄C sample whose composition is Fe rich and near stoichiometric ratio. The characterizations of microstructure demonstrate that the diffusion of B and C atoms into FePt layer depends strongly on B₄C interlayer thickness. When B₄C interlayer thickness of [Fe(2.625 nm)/Pt(3.75 nm)/Fe(2.625 nm)/B₄C]₆ films is bigger than 3 nm, stable value of grain size (6-6.5 nm), coercivity (6-7 kOe) and hardness (16-20 GPa) is observed. Finally, the multifunctional single FePt/B₄C composite film may find its way to substitute traditional three-layer structure commonly used in present data storage technology.