Structure of synthetic calcium hydroxyapatite particles modified with pyrophosphoric acid
Authors:Tanaka Hidekazu  Futaoka Masakazu  Hino Ryozi  Kandori Kazuhiko  Ishikawa Tatsuo
Institution:Department of Material Science, Faculty of Science and Engineering, Shimane University, 1060 Nishikawatsu, Matsue, Shimane 690-8504, Japan. hidekazu@riko.shimane-u.ac.jp
Abstract:Synthetic colloidal calcium hydroxyapatite (Ca(10)(PO(4))(6)(OH)(2): CaHap) was treated with pyrophosphoric acid (H(4)P(2)O(7): PP) in acetone and the materials were characterized by XRD, TEM, FTIR, and N(2) and H(2)O adsorption measurements. XRD patterns and morphology of CaHap particles were essentially not changed by the modification. The additional amount of PO(4) of CaHap was increased with an increase of PP concentration and the Ca/P molar ratio of the particles decreased from 1.62 to 0.81. IR results indicated that the isolated surface POH band developed with increasing the PP concentration up to 6.0 mmol dm(-3) by the reaction of isolated surface POH groups of CaHap and pyrophosphoric acids. Above 10.2 mmol dm(-3), a hydrogen-bonding surface POH band appeared at 2913 cm(-1) and enlarged with increasing the PP concentration, while the isolated surface POH band was weakened. The results of N(2) and H(2)O adsorption measurements revealed that the modified particles aggregated compared to the unmodified ones, which would be due to the formation of hydrogen-bonding surface POH groups among the particles.
Keywords:
本文献已被 PubMed 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号