MgB2 fabrication by diffusion-controlled three layered (B-Mg-B) technique

MgB₂ was successfully fabricated through diffusion-controlled three-layered (B-Mg-B) technique under high pressure. Due to melting temperature of Mg, the material was pre-heat treated at 600 °C between 1 and 48 h. Optimum pre-heat treatment condition was found to be 600 °C for 48 h. Then, the compacted material was grinded and pelletized under pressure of 2 ton. The pellets were heat treated at 600-900 °C for 1-48 h. Optimum heat treatment condition was determined to be 800 °C for 1 h for formation of almost pure MgB₂. Diffusion coefficient was determined with Fick's law and EDX data. Diffusion coefficient value for B in Mg matrix and Mg in B matrix was determined to be 1.66×10⁻⁷ and 3.14×10⁻⁸ cm²/sn, respectively. Best T_c value (39.4 K) was obtained for material heat treated at 800 °C for 1 h. A symmetric hysteresis was obtained for the best MgB₂ material and magnetization decreased with increase in the temperature and the applied magnetic field.