Effects of Na2CO3 flux addition on the structure and photoluminescence properties for Eu-doped YVO4 phosphor

The luminescence properties of (Y_0.9Eu_0.1)VO₄ phosphor with Na₂CO₃ flux prepared using the solid-state reaction were investigated. The XRD patterns show that all of the peaks are attributed to the YVO₄ phase. The best crystallinity was obtained with 2 wt% Na₂CO₃ flux addition. The surface morphology of (Y_0.9Eu_0.1)VO₄ phosphor changed from fluffy to a bar shape structure after Na₂CO₃ flux addition due to the tetragonal crystal system of YVO₄. The calcined powders emit bright red luminescence centered at 618 nm due to the ⁵D₀→⁷F₂ electric dipole transition under an excitation wavelength of 318 nm; its intensity was increased about 15% with 2 wt% Na₂CO₃ flux addition. Red shift behavior was observed for the charge transfer state (CTS) absorption, which was due to the grain size of (Y_0.9Eu_0.1)VO₄ phosphor increasing with increasing flux content. For 2 wt% Na₂CO₃ flux addition, the red emission of the (Y_0.9Eu_0.1)VO₄ phosphor had CIE chromaticity coordinates of (0.66, 0.34), which are very close to the NTSC system standard red chromaticity coordinates of (0.67, 0.33).