Synthesis of mesoporous TiO2 with colloidal gas aphrons,colloidal liquid aphrons,and colloidal emulsion aphrons for dye-sensitized solar cells

High surface area mesoporous titanium dioxide (TiO₂) particles have been prepared by three different kinds of colloidal aphrons: colloidal gas aphrons, colloidal liquid aphrons, and colloidal emulsion aphrons (CEAs). The precipitate of amorphous TiO₂ was prepared by hydrolysis, condensation, and polycondensation reaction of the precursor. The reaction took place under the effect of coulombic repulsion and electrostatic layers of multilayer surfactant molecules. TiO₂ particles with various sizes were prepared with different molar ratio of titanium ion to surfactants, which were sodium lauryl sulfate (SDS), cetyltrimetyhlammonium bromide, triblock copolymer Pluronic P123, and triblock copolymer Pluronic F127. The synthesized samples were characterized by X-ray diffraction, Brunauer-Emmett-Teller analysis, N₂ adsorption/desorption, and transmission electron microscopy. The mesoporous TiO₂ prepared by CEAs method showed a high specific surface area of 224 m²/g with the total pore volume of 0.7751 cm³/g by using SDS as the membrane phase surfactant due to electrostatic attraction favors of anionic surfactant. The solar conversion efficiency of the cell made from TiO₂ increases with the combination of increased surface area and total pore volume for higher amount of dye wetting and loading.