Surface chemical states of gold nanoparticles prepared using the solution-plasma method in a CsCl aqueous solution

In this study, gold nanoparticles (AuNPs) prepared in a 5 mM CsCl aqueous solution using the solution-plasma method are characterized via transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy with synchrotron radiation (SR-XPS). The particle diameter is measured over the process time via TEM. During the solution-plasma process, small particles of 2.1 to 2.2-nm diameter are generated in the CsCl aqueous solution; these particles then enlarge via Ostwald ripening over time until they reach an equilibrium size of ~13 nm after 36 days. In addition, the surface chemical states of the AuNPs are characterized at different depths via SR-XPS. The SR-XPS measurements obtained using incident X-ray energy (hν) of 945.0 eV revealed that Cs─Au, Cl─Au, and Cs─Cl─Au bonds are present 1.2 nm below the surface. The measurements obtained at an incident X-ray energy of 2515.0 eV showed that Cs─Cl─Au bonding is also present 2.5 nm below the surface, indicating that Cs and Cl strongly interact with Au. The TEM and SR-XPS measurements revealed that 2 processes occur cyclically during the growth process via Ostwald ripening: (i) the Cs and Cl in the aqueous solution adsorb on the AuNP surface and (ii) Au atoms subsequently bond to the AuNPs surface.