Preparation and Characterisation of Nano-Structured WO3-TiO2 Layers for Photoelectrochromic Devices

Nano-structured WO₃-TiO₂ layers were prepared by the sol-gel route. To obtain transparent, porous and crack free layers up to 0.8 μ m with a single dipping cycle a templating strategy was used. As a template three-dimensionally network based on organically modified silane was introduced to the WO₃ and TiO₂ sols. The WO₃ layers were dip-coated onto the conductive glass substrate (TCO) and the TiO₂ layers on the top of the WO₃ layer. The morphology and the structure of the layers were determined by Scanning Electron Microscopy (SEM), High Resolution Transmission Electron Microscopy (HR-TEM), Energy Dispersive X-Ray Spectroscopy (EDXS), Auger and Infrared spectroscopy. SEM image of the WO₃-TiO₂ layer confirmed the nano-porosity of the layers and give the size of the particles of about 10 nm for TiO₂ and 30 nm for WO₃ layer. Further analysis indicated that the titanium sol penetrates the WO₃ layer. Particles in the WO₃ layer consist of a crystalline monoclinic WO₃ core surrounded by a 5–10 nm amorphous phase consisting of WO₃, TiO₂ and SiO₂. The WO₃-TiO₂ layers were used to assemble all solid state photoelectrochromic (PE) devices. Under 1 sun irradiation (1000 W/m²) the visible transmittance of the PE device changes from 62% to 1.6%. The colouring and bleaching processes last about 10 minutes.