Mechanism of formation of YBa2Cu4O8 superconductor in the sol-gel synthesis

It was shown that a single phase YBa₂Cu₄O₈ (124-phase) could be formed from gels at 1 atm oxygen pressure, and the mechanism of its formation was elucidated. It was found that there are two key routes for the sol-gel formation of the 124-phase, one involving the tetragonal YBa₂Cu₃O _y with a low concentration of oxygen defects (tetra-I phase) and the other involving the Ba₂Cu₃O_5.9 as important intermediates of the 124-phase. The rapid formation of these intermediate compounds from the gel was attributed to the small particle size of the oxides and carbonates precipitating at the initial stage of heating. It was thought that the small particles characteristic of sol-gel processing lead to the rapid formation of the intermediate compounds and subsequent precipitation of the 124-phase.