Low‐temperature sol–gel transformation of methyl silicon precursors to silica‐based hybrid materials

Six new methyl silicon (IV) precursors of the type MeSi{ON?C(R)Ar}₃] when R = Me, Ar = 2‐C₅H₄N ( 1 ), 2‐C₄H₃O ( 2 ) or 2‐C₄H₃S ( 3 ); and when R = H, Ar = 2‐C₅H₄N ( 4 ), 2‐C₄H₃O ( 5 ) or 2‐C₄H₃S ( 6 )] were prepared and structurally characterized by various spectroscopic techniques. Molecular weight measurements and FAB (Fast Atomic Bombardment) mass spectral studies indicated their monomeric nature. ¹H and ¹³C{¹H} NMR spectral studies suggested the oximate ligands to be monodentate in solution, which was confirmed by ²⁹Si{¹H} NMR signals in the region expected for tetra‐coordinated methylsilicon (IV) derivatives. Thermogravimetric analysis of 1 revealed the complex to be thermally labile, decomposing to a hybrid material of definite composition. Two representative compounds ( 2 and 4 ) were studied as single source molecular precursor for low‐temperature transformation to silica‐based hybrid materials using sol–gel technique. Formation of homogenous methyl‐bonded silica materials (MeSiO_3/2) at low sintering temperature was observed. The thermogravimetric analysis of the methylsilica material indicated that silicon‐methyl bond is thermally stable up to a temperature of 400 °C. Reaction of 2 and Al(OPrⁱ)₃ in equimolar ratio in anhydrous toluene yielded a brown‐colored viscous liquid of the composition MeSi{ON?C(CH₃)C₄H₃O}₃.Al(OPrⁱ)₃]. Spectroscopic techniques ¹H, ¹³C{¹H}, ²⁷Al{¹H} and ²⁹Si{¹H} NMR spectra of the viscous product indicated the presence of tetracoordination around both silicon and aluminum atoms. On hydrolysis it yielded methylated aluminosilicate material with high specific surface area (464 m²/g). Scanning electron micrography confirmed a regular porous structure with porosity in the nanometric range. Copyright © 2008 John Wiley & Sons, Ltd.