Some physical and magnetic properties of Mg‐Zn ferrite

Some physical properties (such as lattice parameter, density and porosity) and magnetic properties of the system Mg_1‐xZn_xFe₂O₄; where x=0,0.1,0.2,0.3,0.4,0.5and 0.6 have been studied. It was found that the lattice parameter increases with increasing the zinc concentration. The composition dependence of the physical properties is divided into two regions. The first one is for x ≤ 0.3 and the second one is for x > 0.3. From the magnetization measurements, the basic composition (MgFe₂O₄) shows the lowest magnetization, while the composition of x=0.4 shows the highest one. The behaviour of magnetization M versus composition shows also two regions for x <>0.3. The behaviour of M versus x was discussed in the bases of cation distribution. From the B‐H loops, the remanence induction B_r, saturation induction B_s and the coercive force H_c were determined and studied with x. The Curie temperature T_C was determined from the measurements of the initial permeability μ_i versus temperature. It was found T_C decreases with increasing Zn‐content. Also paramagnetic temperature T_P was determined from the behaviour of M_S vs. T. In general it was found T_P > T_C by about 7‐10 K.