| Abstract: | The composition of an ethylene-propylene block copolymer with a nominal 15% content of ethylene by weight (EP?B15%) has been investigated through fractionation near the lower critical solution temperature (LCST). Observation of the solution heated above the boiling point of the solvent indicated that some polymer was phase separating, apparently continuously, between the LCSTs of polyethylene (PE) an polypropylene (PP) of similar molecular weight. IR and DSC analysis of three fractions obtained by twice separating the concentrated phase from the dilute phase gave the following result: EP?B15% consists of an ethylene-rich block copolymer (93% E), an EP copolymer of intermediate composition, and a propylene-rich copolymer (94% P). The three fractions constitute respectively 12%, 12%, and 76% of the total weights. In order to choose a suitable temperature for fractionation, a turbidity analysis of the solution of the initial polymer is made continuously during phase separation. The trace of turbidity against temperature shows three peaks of turbidity at temperatures T0, T1 and T2, which can be associated with the above fractions. A mixture of PE, PP, and a 33% E random copolymer gives a turbidity trace with characteristic temperatures very similar to that of EP-B15% in the same solvent. Fractionation from several solvents or mixtures of solvents indicated that the composition of the fractions did not depend significantly on the nature of the solvent. Conditions for obtaining a quantitative analysis of a mixture from a thermogram are discussed. Turbidity analysis during phase separation and fractionation at the LCST can be a useful tool in analyzing and separating complex mixtures before use of powerful analytical techniques such as NMR or IR spectroscopy. |