A partial phase diagram for a mixture of polystyrene with a low molecular weight styrene-dimethylsiloxane block copolymer

Differential scanning calorimetry (DSC) was used to examine the miscibility of polystyrene (PS), mol. wt. 10⁵, with a phase-separated styrene-dimethylsiloxane (S-DMS) diblock copolymer, M_n = 3800, 86 wt% S. Mixtures whose S content varied from 4 to 96 wt% PS were examined at a 10 K min^?1 heating rate following a 200 K min^?1 cooling rate from temperatures varying from 403 to 573 K. At some compositions, two glass transition temperatures, T_gs, corresponding to PS transitions were observed; at others only a single T_g was observed. When it was assumed that the 200 K min^?1 cooling rate corresponded to quenching from the starting temperature, and when the heat capacity changes at the S glass transitions were used to calculate the percentage of S repeat units undergoing each glass transition, it was possible to calculate an approximate partial phase diagram for this mixture. At 96 wt% PS, there was evidence for a small amount of mixed S phase, possibly block copolymer micelles, in equilibrium with PS; from about 60 to 90 wt% PS, the S repeat units from the block copolymer appeared to be completely mixed with the PS. At lower wt% PS, unmixed block copolymer was in equilibrium with block copolymer whose S segments were mixed with the PS. The phase diagram appeared to vary only slightly with temperature.