| Abstract: | The aqueous polymerization of methyl methacrylate was carried out in the absence and in presence of corundum or carborundum at 25 and 80°C. In the absence of corundum and carborundum, it has been found that rising the polymerization temperature from 25 to 80°C resulted in changing the tacticity of the obtained polymers. At 25°C the isotactic triad was 26% while the heterotactic triad was 33.5% and the syndiotactic one was 40.5%. Increasing the polymerization temperature to 80°C resulted in a decrease of the isotactic structure to 0% and increased the heterotactic structure and syndiotactic structure to 48 and 52% respectively. Polymerizing at 25°C in presence of corundum (0.5 g) an increase in the syndiotactic triad took place from 40.5 to 50.7% while the isotactic triad decreased from 26 to 22.2% and the heterotactic structure decreased from 33.5 to 27%. Raising the polymerization temperature to 80°C in the presence of the same amount of corundum resulted in an increase in both the isotactic and heterotactic triads to 35 and 32.7%, respectively. Polymerizing at 80°C in presence of corundum (0.5 g) resulted in nearly an equal percentage of each triad 33%. |