Thermochemical property of a microporous material for mixed metal borate of Li2Sr4B12O23 |
| |
Authors: | Wenjie Zheng Dawei Li |
| |
Institution: | 1. School of Pharmacy, Shanghai Jiao Tong University, Shanghai, 200240, People’s Republic of China
|
| |
Abstract: | A pure mixed alkali–alkaline earth metal borate of Li2Sr4B12O23 with microporous structure has been synthesized by high-temperature solid state reaction, and characterized by XRD, FT-IR, TG techniques, and chemical analysis. The molar enthalpies of solution of Li2Sr4B12O23 in 1 mol L?1 HCl(aq), and of SrCl2·H2O(s) in 1 mol L?1 HCl + H3BO3 + LiCl·H2O](aq) have been determined by microcalorimeter at 298.15 K, respectively. From these data and with the incorporation of the previously determined enthalpies of solution of H3BO3(s) in 1 mol L?1 HCl(aq), and of LiCl·H2O(s) in 1 mol L?1HCl + H3BO3](aq), together with the use of the standard molar enthalpies of formation for SrCl2·6H2O(s), LiCl·H2O(s), H3BO3(s), HCl(aq), and H2O(l), the standard molar enthalpy of formation of ?(11,534.0 ± 10.0) kJ mol?1 for Li2Sr4B12O23 was obtained on the basis of the appropriate thermochemical cycle. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|