Influence of organic dyes on the thermal,mechanical, and optical properties of l-arginine trifluoroacetate (LATF) single crystals

Bulk single crystals of pure and organic dyes (rhodamine, amaranth, and methyl orange) admixture l-arginine trifluoroacetate were grown by slow evaporation technique. The cell parameters and crystallinity of pure and dyes-mixed LATF were confirmed by powder X-ray diffraction analysis. Thermal analysis (TG/DTA, DSC) reveals the purity of the sample and no decomposition is observed up to melting point. In the TG trace of pure LATF, methyl orange: LATF, amaranth: LATF and rhodamine: LATF it is observed that the crystals were thermally stable up to 488, 485, 483, and 484.14 K, respectively. The crystals are further characterized using UV–Vis analysis, microhardness analysis, and EDAX analysis. By plotting log P versus log d, the value of the work hardening coefficient "n" was found to be 1.95, 0.52, 0.8, and 0.88 for pure, methyl orange, amaranth, and rhodamine dyes-doped LATF grown crystals, respectively. Second harmonic generation efficiency of pure and dye admixture LATF crystals was measured using Kurtz and Perry powder test, the efficiency of methyl orange, amaranth, and rhodamine dyes-doped LATF crystal is 2.7, 2.6, and 2.07 times greater than KDP, where as the efficiency of LATF pure is 2.5 times greater than that of KDP.