Antiferromagnetic Mn50Fe50 wire with large magnetostriction

This work presents a study on the relation between the fiber texture and the magnetostrictive performance in an antiferromagnetic Mn₅₀Fe₅₀ alloy wire, which was prepared through the combining process of hot rolling and cold drawing. The face-centered cubic (fcc) crystal structure can be retained during the plastic deformation process. Mixed fiber textures consisting of both 1 1 0 and 1 0 0 components were formed along the drawing direction (DD) in the wire. A large magnetostriction of 750 ppm was obtained along DD under 1.2 T, which can be ascribed to the single γ phase and the formation of preferred crystal orientation.