Orientation effects in nanoindentation of single crystal copper

Numerical simulations and experimental results of nanoindentation on single crystal copper in three crystallographic orientations (1 0 0), (0 1 1) and (1 1 1)] using a spherical indenter (3.4 μm radius) were reported. The simulations were conducted using a commercial finite element code (ABAQUS) with a user-defined subroutine (VUMAT) that incorporates large deformation crystal plasticity constitutive model. This model can take full account of the crystallographic slip as well as the orientation effects during nanoindentation. Distributions of the out-of-plane displacements and shear stresses as well as shear strains were obtained for indentation depths of up to 310 nm. The experimental studies were conducted using an MTS Nano Indenter (XP) system from which the load–displacement relationships were obtained while the surface topography as well as the surface profile along a line scan of indents were obtained using a Digital Instruments (Dimension 3100) atomic force microscope (AFM). The top views of the indent pile-up patterns under the spherical indenter show two-fold, three-fold, and four-fold symmetries for the (0 1 1), (1 1 1), and (1 0 0) orientations, respectively. Attempt was made to relate the anisotropic nature of the surface topographies around the indents in different crystallographic orientations of the single crystal copper specimens with the active slip systems and local texture variations. A reasonably good agreement had been obtained on several aspects of nanoindentation between the experimental and numerical results reported in this investigation as well as similar results reported in the literature. Thus, material properties of single crystal copper can be determined based on an appropriate numerical modeling of the nanoindentation on three crystallographic orientations.