Properties of sulfonated poly(butylene terephthalate)

The synthesis, morphology, and mechanical properties of sulfonated poly(butylene terephthalate) (PBT) and its unsulfonated analogs were studied. The morphology of these copolymers crystallized from the melt were examined by a combination of wide-angle x-ray scattering (WAXS), polarized light microscopy, and small-angle light scattering (SALS). Stress-strain measurements are correlated with the morphological results. Spherulitic morphology, with a maltese cross at 45°C with respect to the crossed polars, is formed at low sulfonate levels (≤ 5.0 mol %). At a higher ion content, the maltese cross rotates 45° to form a cross pattern. At still higher sulfonate contents, typically 13 mol %, the light scattering pattern disappears completely. Microscopic and WAXS examination of these functionalized PBT copolymers confirms that the crystallinity level decreases with increasing ion content and is eliminated completely at the higher sulfonation level. The spherulite radius, however, remains invariant until the highest functionalization level. On the contrary, the morphology and properties of the unsulfonated isophthalate copolymer analogs remain relatively constant over the entire composition range examined. In several compositions clearly inferior properties are noted compared with the ion-containing copolymers.