Controlled Synthesis of Hollow PbS‐TiO2 Hybrid Structures through an Ion Adsorption–Heating Process and their Photocatalytic Activity

Hollow hybrid nanostructures have received significant attention because of their unique structural features. This study reports a facile ion adsorption–heating method to fabricate hollow PbS‐TiO₂ hybrid particles. In this method, the TiO₂ spheres used as a substrate material to grow PbS are aggregates of many small amorphous TiO₂ particles, and each small particle is covered with thioglycolic acid ligands through Ti⁴⁺–carboxyl coordination. When Pb²⁺ ions are added to a colloidal solution of these TiO₂ spheres, these ions are adsorbed by sulfhydryl (‐SH) groups to form metal thiolates, and the C−S bond is dissociated by heating to release S²⁻. The S²⁻ ions react with Pb²⁺ ions to form PbS without additive sulfur sources. Additionally, the amorphous TiO₂ spheres are transformed into the anatase phase during the heating process. As a result, the crystallization of TiO₂ spheres along with the formation of PbS is simultaneously carried out by heating. During the heating process, owing to the Kirkendall effect of S²⁻ diffusion and the Ostwald ripening effect of the crystallization of amorphous TiO₂ spheres, PbS‐TiO₂ hollow hybrid structures can be obtained. The XRD and XPS characterizations proved the formation of anatase TiO₂ and PbS. The TEM characterization confirmed the formation of hollow structures in the PbS‐TiO₂ hybrid sample. The photocatalytic activity of the hollow PbS‐TiO₂ hybrid spheres have been investigated for the degradation of Cr⁶⁺ under visible light. The results show that hollow PbS‐TiO₂ hybrid spheres exhibited the highest photocatalytic activity, in which almost all the Cr⁶⁺ was degraded after 140 min.