SWELLING BEHAVIOR OF ACRYLAMIDE HYDROGEL IN DIFFERENT SOLVENTS AND pHs

Swelling property of acrylamide hydrogels, prepared from aqueous solutions of acrylamide monomer having concentrations in the range of 10-60 wt% by γ-ray irradiation method using a Co-60 gamma radiation source at doses ranging 1-30.0 kGy, has been investigated under various swelling media. These swelling media were basically solvents (solutions), produced by dissolving methanol, ethanol, glucose, sucrose, sodium chloride and sodium persulfate individually with distilled water, and solutions prepared with pHs = 3, 7 and 10. The investigation was performed in order to observe the effect of these solvents and pHs as well as the influence of monomer concentrations, radiation doses and times on swelling behavior of hydrogels. Swelling values were found higher for hydrogels prepared with lower monomer concentrations (ca.20 wt%) and radiation doses (ca. 5 kGy) and showed a leveling off tendency within 24 h. The glucose solvent and the buffer solution of pH = 10 revealed significant increase of swelling of hydrogels as compared to other solutions. Results are explained based on crosslinking density in hydrogel, polymer-solvent/polymer-polymer interactions in solutions,permeability of molecules in solutions and ionization capacity of hydrogel in pH.

SWELLING BEHAVIOR OF ACRYLAMIDE HYDROGEL IN DIFFERENT SOLVENTS AND pHs

Swelling property of acrylamide hydrogels, prepared from aqueous solutions of acrylamide monomer having concentrations in the range of 10-60 wt% by γ-ray irradiation method using a Co-60 gamma radiation source at doses ranging 1-30.0 kGy, has been investigated under various swelling media. These swelling media were basically solvents (solutions), produced by dissolving methanol, ethanol, glucose, sucrose, sodium chloride and sodium persulfate individually with distilled water, and solutions prepared with phs = 3, 7 and 10. The investigation was performed in order to observe the effect of these solvents and phs as well as the influence of monomer concentrations, radiation doses and times on swelling behavior of hydrogels. Swelling values were found higher for hydrogels prepared with lower monomer concentrations (ca.20 wt%) and radiation doses (ca. 5 kGy) and showed a leveling off tendency within 24 h. The glucose solvent and the buffer solution of pH = 10 revealed significant increase of swelling of hydrogels as compared to other solutions. Results are explained based on crosslinking density in hydrogel, polymer-solvent/polymer-polymer interactions in solutions,permeability of molecules in solutions and ionization capacity of hydrogel in pH.