Synthesis and photoluminescence stability of non-conjugated polymers based on fluorene and benzoxazole |
| |
| Authors: | Xiaohui Xu Xiaoyun Liu Qixin Zhuang |
| |
| Institution: | a Key Laboratory for Specially Functional Polymeric Materials and Related Technology of the Ministry of Education, School of Materials Science and Engineering, East China University of Science and Technology, Shangha 200237i, China
b College of Material Science and Engineering, Tsinghua University, Beijing 100084, China |
| |
| Abstract: | A kind of non-conjugated blue luminescent polymer based on fluorene and benzoxazole was synthesized via solution condensation polymerization from 2,2-bis(3-amino-4-hydroxyphenyl)-propane and 2,7-dicarboxyl-9,9-dioctyl-fluorene and was characterized with H NMR, FT-IR, thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), UV-vis absorption and photoluminescence (PL) spectroscopy. The polymer displayed the maximum photoluminescence emission peak at 415 nm and showed high PL spectroscopic stability. The green-to-blue emission intensity ratio IGreen/IBlue is only 0.073 even after thermal annealing at 150 °C for 30 h. After being exposed to UV light for 30 min, no bathochromic emission or obvious crosslink is observed. The common phenomenon of greenish blue emission of fluorene-based polymer around 525 nm has been effectively restrained in this polymer by introducing the isopropylidene group into the backbone of polymer. |
| |
| Keywords: | Non-conjugated polymer Fluorene Benzoxazole Spectral stability Synthesis |
| 本文献已被 ScienceDirect 等数据库收录！ |
|