Studies on the copolymerisation of N-isopropyl-acrylamide with glycidyl methacrylate

The paper describes the homopolymerisation and copolymerisation of N-isopropyl acrylamide (NIPAM) with glycidyl methacrylate (GMA) in solution at 60°C using azobisisobutyronitrile (AIBN) as an initiator and dioxan as solvent. Copolymers were synthesized by varying the mol fraction of GMA in the initial feed from 0.025-0.125. All the polymerization reactions were terminated at low % conversion (10-15%) and the copolymer composition was determined by measuring the epoxy content. Percent epoxy content was determined by titration method using pyridine-HCl mixture. The reactivity ratios determined using Fineman-Ross method were found to be 0.94±0.05 (r₁, NIPAM) and 1.05±0.08 (r₂, GMA). All the polymers have high molecular weights with wide molecular weight distribution as determined by gel permeation chromatography (GPC) i.e. M_n in the range of 3.7 x 10⁴ - 7.8 x 10⁴ and M_w in the range of 1.2 x 10⁵ - 4.1 x 10⁵ with a polydispersity index in the range of 2.3-5.3. Lower critical solution temperature (LCST) of NIPAM homopolymer and copolymers was determined by recording DSC scans of polymers in aqueous solution. Incorporation of GMA in the poly(NIPAM) backbone resulted in a decrease in the LCST.