RUPTURING OF POLYMER FILMS WITH RUBBING-INDUCED SURFACE DEFECTS

It has been a long-standing question whether dewetting of polymer film from non-wettable substrate surfaceswherein the bicontinuous morphology never forms in the dewetting film is due to spinodal instability or heterogeneousnucleation. In this experiment, we use a simple method to make the distinction through introduction of topographical defectsof the films by rubbing the sample surface with a rayon cloth. Spinodal dewetting is identified for those films that dewet by acharateristic wavevector, q, independent of the density of rubbing-induced defects. Heterogeneous nucleation, on the otherhand, is identified for those with q increasing with increasing density of defects. Our result shows that PS films on oxidecoated silicon with thickness less than ≈ 13 nm are dominated by spinodal dewetting, but the thicker films are dominated bynucleation dewetting. We also confirm that spinodal dewetting does not necessarily lead to a bicontinuous morphology in thedewetting film, contrary to the classic theory of Cahn.

RUPTURING OF POLYMER FILMS WITH RUBBING-INDUCED SURFACE DEFECTS

 It has been a long-standing question whether dewetting of polymer film from non-wettable substrate surfaceswherein the bicontinuous morphology never forms in the dewetting film is due to spinodal instability or heterogeneousnucleation. In this experiment, we use a simple method to make the distinction through introduction of topographical defectsof the films by rubbing the sample surface with a rayon cloth. Spinodal dewetting is identified for those films that dewet by acharateristic wavevector, q^*, independent of the density of rubbing-induced defects.Heterogeneous nucleation,on the other hand,is identified for those with q^* increasing with increasing density of defects.Our result shows that PS films on oxide coated silicon with thickness less than ≈13 nm are dominated by spinodal dewetting,but the thicker films are dominated by nucleation dewetting.We also confirm that spinodal dewetting does not necessarily lead to a bicontinuous morphology in the dewetting film,contrary to the classic theory of Cahn.