Effects of low-LET radiations on CR-39 track detector

The effects of Co-60 gamma-rays and about 25-MeV pulsed electrons have been investigated on CR-39 plastic nuclear track detector. The bulk etch rate was measured as a function of the absorbed dose under three different irradiation conditions; gamma-ray exposure in air at the dose rate of 6 kGy/h, that in vacuum and electron shower in air at 126 kGy/h on average. It was found that the bulk etch rate (V) increased nearly exponentially with the dose (D); V=V₀exp(kD), and the characteristic parameter (k) was 35, 9 and 12 MGy⁻¹, respectively. It is considered that a lack of oxygen in damage formation processes could occur momentarily during a short electron pulse, just similarly to the vacuum effect of reduction in track etch rates in outgassed CR-39 plastic.