Spectral properties and temperature-dependence of semiconductivity of various doped bismuth trioxide polycrystals |
| |
| Authors: | M. M. Abou Sekkina E. El-Shereafy |
| |
| Affiliation: | (1) Faculty of Science, Tanta University, Tanta, Egypt;(2) Faculty of Science, El-Monoufeia University, Shibin El-Kom, Egypt;(3) Present address: Faculty of Science, The United Arab Emirates University, P.O. box 15551, Al-Ain, U.A.E. |
| |
| Abstract: | Several samples of Nb2O5-doped Bi2O3 and Y2O3-doped Bi2O3 were carefully prepared and sintered at 700° for 3 hours. Extensive measurements were carried out on these samples, including X-ray diffraction spectra, infrared absorption spectra and the temperature-dependence of the DC-electrical conductivity in the solid state. The results obtained were discussed, correlated and interpreted. Finally, the optimum compositions were established and recommended for doped-Bi2O3 in the electronics industry.
Zusammenfassung Einige Proben von mit Nb2O5 und Y2O3 gedopten Bi2O3 wurden hergestellt und bei 700 °C 3 Stunden gesintert. Von den Proben wurden Röntgendiffraktogramme und IR-Absorptionsspektren aufgenommen und die Temperaturabhängigkeit der elektrischen Gleichstromleitfähigkeit im festen Zustand gemessen. Die erhaltenen Ergebnisse werden diskutiert, zueinander in Beziehung gesetzt und interpretiert. Optimale Zusammensetzungen werden ermittelt und für gedoptes Bi2O3 in der Elektronikindustrie empfohlen.
                Bi2O3,      Nb2O5 Y2O3,     3 700°.     ,   .  . ,  .
|
| |
| Keywords: | |
| 本文献已被 SpringerLink 等数据库收录！ |
|