| Abstract: | Pure gas sorption and transport properties of polyesters based on bisphenol-A and both pure isophthalic and pure terephthalic acid chloride were obtained for He, N2, O2, CH4, and CO2 at 35°C. The polymers were synthesized in our laboratory and amorphous films were prepared with a specialized solvent casting procedure. The polymer containing m-phenylene groups shows higher permselectivity for most of the gas pairs. The ideal selectivity of O2/N2 was increased by 33% when p-phenylene units were replaced by m-phenylene ones. On the other hand, the polyester containing only p-phenylene groups, shows higher permeability to all the gases studied. The polymer based on pure terephthalic acid chloride has a 75% higher oxygen permeability and a 1.1-fold higher carbon dioxide permeability than the isophthalic acid derivative. The polyester containing meta-phenylene units has lower Tg, higher permselectivity, lower permeability, lower fractional free volume (FFV), and lower d-spacing. The values of FFV, and lower d-spacing. The values of FFV and d-spacing were only slightly different between the two isomers. Moreover, for the sub-Tgγ transition the maximum in tan δ occured at essentially the same temperature (?55°C). The polymer with a higher concentration of p-phenylene units shows somewhat larger area under the γ-peak, indicating slightly more sub-Tg motion. The Distribution of FFV is considered to be the determining factor for the differences in transport properties observed. © 1993 John Wiley & Sons, Inc. |