Modification of polybenzimidazole: Synthesis and thermal stability of poly(N1-methylbenzimidazole) and poly(N1,N3-dimethylbenzimidazolium) salt

Poly(N₁,N₃-dimethylbenzimidazolium) (PDMBI) salt and poly(N₁-methylbenzimidazole) (PMMBI) were synthesized by methylation of commercial polybenzimidazole [poly-2,2′-(m-phenylene)-5,5′-bibenzimidazole (PBI)]. First, the N-lithium salt of polybenzimidazole was formed by treating polybenzimidazole solution of 1-methyl-2-pyrolidinone (NMP) with lithium hydride at 80°C for 18 h. Ninety percent substitution of PMMBI was obtained by treating the N-lithium salt of PBI with equimolar ratio of iodomethane at room temperature. Upon addition of excess iodomethane to the lithium salt of PBI at 80°C, a polymer was formed that showed 100% substitution on the N₁ nitrogen and about 30% substitution of the methyl group on the N₃ nitrogen in the form of N₁,N₃-dimethylbenzimidazolium iodide salt [PDMBI (30%)]. The content of the benzimidazolium iodide salt was increased to about 90% by dissolving PDMBI (30%) in dimethyl sulfoxide (DMSO) and re-treating with excess iodomethane at 80°C overnight. The modified PBI polymers were characterized by NMR and FTIR. The modified PBI differed in solubility from PBI. PMMBI could be easily dissolved in NMP and PDMBI in DMSO at room temperature. The solution of PDMBI could be mixed with water in all proportions without precipitation. PDMBI could be also dissolved directly in a mixture of DMSO and water (1 : 1). Typical polyelectrolyte behavior of viscosity was found in solution of PDMBI (30%) and PDMBI (90%) when DMSO and a mixture of DMSO and water were used as solvents. A salt effect on viscosity was also found in the mixed solvent solution. Thermogravimetric analysis (TGA) showed that the methyl group on the imidazole ring was unstable above 180°C under nitrogen. When PDMBI was heated under nitrogen, one of the methyl groups was lost with the counterion to result in a neutral PMMBI. © 1993 John Wiley & Sons, Inc.