Abstract: | First, the general concept of the “Precursor Method” for the preparation of polymeric Langmuir-Blodgett (LB) films that possess no long alkyl chain between film layers, and the preparation of polybenzothiazole 7 LB film are described. The preparation of 7 LB film was carried out by the same procedure as that used to make polyimide LB films via precursor LB films of polyamides that contain β-carboxyethylthio alkylamine salts 6. Precursor 6 LB film had a Y type structure with monolayer thickness of 2.8 nm, while polybenzothiazole 7 LB film had 0.34 nm. The nonlinear susceptibility χ(3) of polybenzothiazole 7 LB film in parallel to the dipping direction was 3.8 × 10−11 esu, whereas the susceptibility in the perpendicular direction was about one fifth of that of the parallel direction. |