Spin probe studies on high temperature (T >T
g) microdynamics of polyamide 66 fibers |
| |
Authors: | P Törmälä |
| |
Institution: | (1) Institute of Materials Science, Tampere University of Technology, Tampere, Finland |
| |
Abstract: | Summary Short-range segmental motions of the amorphous phase of polyamide 66 were studied by means of spin probe radicals. In a dry sample the relaxation in the temperature range 366–426 with an activation energy 27.6 kJ/mol was found. In a sample containing traces of water two processes, and relaxations, with activation energies 47.0 kJ/mol and 22.0 kJ/mol, respectively, were found. relaxation was dominant in the higher temperature range (410–460 K) while relaxation was active at lower temperatures (365–410 K).
Zusammenfassung Die inneren, lokalen Drehbewegungen in den amorphen Bereichen des Polyamid 66 wurden mit Hilfe der Paramagnersondenmethode untersucht. Wasserfreies Polyamid 66 zeigt den -Relaxations-prozeß (die Aktivierungsenergie 27.6 kJ/Mol) im Temperaturbereich von 366 K bis 426 K, wasserhaltiges Polyamid 66 zeigt zwei Prozesse, - und -Relaxationen, deren Aktivierungsenergien 47.0 kJ/Mol und 22.0 kJ/Mol sind. Die -Relaxation dominiert in dem höheren Temperaturbereich (von 410 K bis 460 K) und die -Relaxation in dem niederen Temperaturbereich (von 365 K bis 410 K). |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|