Magnetic and microwave absorbing properties of magnetite-thermoplastic natural rubber nanocomposites

Magnetic and microwave absorbing properties of thermoplastic natural rubber (TPNR) filled magnetite (Fe₃O₄) nanocomposites were investigated. The TPNR matrix was prepared from polypropylene (PP), natural rubber (NR) and liquid natural rubber (LNR) in the ratio of 70:20:10 with the LNR as the compatibilizer. TPNR-Fe₃O₄ nanocomposites with 4-12 wt% Fe₃O₄ as filler were prepared via a Thermo Haake internal mixer using a melt-blending method. XRD reveals the presence of cubic spinel structure of Fe₃O₄ with the lattice parameter of a=8.395 Å. TEM micrograph shows that the Fe₃O₄ nanoparticles are almost spherical with the size ranging 20-50 nm. The values of saturation magnetization (M_S), remanence (M_R), initial magnetic susceptibility (χ_i) and initial permeability (μ_i) increase, while the coercivity (H_C) decreases with increasing filler content for all compositions. For nanocomposites, the values of the real (ε_r′) and imaginary permittivity (ε_r′′) and imaginary permeability (μ_r′′) increase, while the value of real permeability (μ_r′) decreases as the filler content increases. The absorption or minimum reflection loss (R_L) continuously increases and the dip shifts to a lower frequency region with the increasing of both filler content in nanocomposites and the sample thickness. The R_L is −25.51 dB at 12.65 GHz and the absorbing bandwidth in which the R_L is less than −10 dB is 2.7 GHz when the filler content is 12 wt% at 9 mm sample thickness.