Structural transformations and magnetic properties of Fe60Pt15B25 and Fe60Pt25B15 nanocomposite alloys

Structural and magnetic properties of two rapidly solidified and post-annealed Fe₆₀Pt₁₅B₂₅ and Fe₆₀Pt₂₅B₁₅ alloys are compared. The as-quenched Fe₆₀Pt₁₅B₂₅ ribbon was fully amorphous whereas in the Fe₆₀Pt₂₅B₁₅ alloy the amorphous phase coexists with an fcc FePt disordered solid solution. Differential scanning calorimetry curves of both alloys reveal a single exothermal peak with onset temperatures of 873 and 847 K for Fe₆₀Pt₁₅B₂₅ and Fe₆₀Pt₂₅B₁₅, respectively. Magnetically hard, tetragonal ordered L1₀ FePt and magnetically soft Fe₂B nanocrystalline phases were formed due to the annealing of the alloys, as indicated by X-ray diffraction and Mössbauer spectroscopy measurements. Two-phase behavior was detected in the temperature dependence of magnetization of the annealed samples. A magnetic hardening was observed for all annealed ribbons. Magnetic properties of the annealed alloys, studied by hysteresis loop measurements, were related to the differences in the relative fractions of the hard and soft magnetic phases calculated from Mössbauer spectra. The alloy with 25 at% Pt exhibits better hard magnetic properties (H_c=437 kA/m, M_r/M_s=0.74) than the alloy with smaller Pt content (H_c=270 kA/m, M_r/M_s=0.73) mainly due to the larger abundance of the ordered tetragonal FePt phase.