Ti deficiency effect on the dielectric response of CaCu3Ti4O12 ceramics

Single phase ceramics CaCu₃Ti_4.0O₁₂ and CaCu₃Ti_3.9O₁₂ have been prepared using the traditional solid-state reaction method. Compared with the stoichiometric ceramics CaCu₃Ti_4.0O₁₂, Ti-deficient ceramics CaCu₃Ti_3.9O₁₂ have the larger lattice parameter, the higher force constant, and smaller dielectric constant and the lower dissipation factor, although their fundamental characters of dielectric response are similar. Their characteristic relaxation frequencies are not well fitted with the Arrhenius Law but a tentatively supposed relation. With the Cole-Cole Law, the fitted broadened factors of dissipation peaks are 0.5433 and 0.8651 for CaCu₃Ti_3.9O₁₂ and CaCu₃Ti_4.0O₁₂, respectively. All facts mentioned above imply that mutually correlated motion of Ti ions or defects may be expected to be responsible for the giant dielectric constant and high dissipation factor of CaCu₃Ti_4.0O₁₂.