Preparation and properties of silylated PTFE/SiO2 organic–inorganic hybrids via sol–gel process

A study on poly(tetrafluoroethylene) (PTFE) reinforced with tetraethoxysilanes (TEOS) derived SiO₂ is described. It included the manufacturing process of SiO₂‐reinforced PTFE and the effects of silylation agent on the properties of the hybrid material, such as porosity, hydrophobic, thermal resistance, dielectric and mechanical properties, and microstructure. PTFE/SiO₂ hybrids of 50 wt % SiO₂ loading were prepared via a sol–gel process and were shaped by a two‐roll milling machine. Trimethylchlorosilane and hexamethydisilazane were used as the silylation agents. Our results showed that the water absorption and dielectric loss of PTFE/SiO₂ hybrid had significantly improved with silylation agent. The silylation process replaced Si? OH with Si? CH₃ on the surface of the TEOS‐derived silica colloidal particle. The existence of trimethylsilyl ? Si(CH₃)₃] on the surface of the modified PTFE/SiO₂ hybrid was confirmed via infrared and solid‐state ²⁹Si magic‐angle spinning nuclear magnetic resonance spectra. Nitrogen‐sorption techniques were used to characterize the modified and unmodified PTFE/SiO₂ hybrids. The microstructure of SiO₂ in the matrix was also evaluated with scanning electron microscopy and transmission electron microscopy. Our results showed that the silylated sol–gel‐derived PTFE/SiO₂ hybrids had exhibited high porosity (53.7%) with nanosize pores (10–40 nm) and nanosize colloidal particles (20–50 nm). This manifests itself as have the ultralow dielectric properties (D_k = 1.9 and D_f = 0.0021), low coefficient of thermal expansion (66.5 ppm/°C), high tensile modulus (141 MPa), excellent thermal resistance (T_d = 612 °C), and an increased hydrophobia (θ = 114°); moreover, the hydrophobic property of the PTFE/SiO₂ hybrid was thermally stable up to 400 °C. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1789–1807, 2004