Synthesis and characterization of original functional polymers of tetrafluoroethylene and 4,5,5‐trifluoro‐4‐ene pentyl acetate

The bulk radical copolymerization of tetrafluoroethylene (TFE) with 4,5,5‐trifluoro‐4‐ene pentyl acetate (FAc), initiated by tert‐butyl peroxypivalate to synthesize original, functionalized fluorinated poly(TFE‐co‐FAc), was investigated. FAc monomer was prepared from a five‐step process. The copolymerization was carried out in batch at different initial monomer molar ratios (TFE]_o/FAc]_o ranging from 95/5 to 10/90 mol %) and at different initiator concentrations (ranging between 0.075 and 1.100 mol % about the monomers) at 70 °C. All the experiments revealed the production of fluorooligomers as evidenced by an allylic‐transfer reaction from FAc. The microstructure of these copolymers (i.e., the molar percentage of both monomers in the copolymers) was assessed by ¹⁹F NMR spectroscopy. From the kinetics of copolymerization, two key characteristics were determined. First, the reaction order to the initiator (being 1.07) and that of FAc monomer (0.85) showed a heterogeneous character of the copolymerization and monomolecular chain‐transfer reaction to FAc. Second, from the Tidwell and Mortimer method, the reactivity ratios of both comonomers were determined, showing a tendency to alternance in a wide range of initial monomeric ratios (30/70–70/30): r_FAc = 0.20 ± 0.26 and r_TFE = 0.18 ± 0.15. Alfrey and Price's Q and e values of FAc were calculated by Greenley's technique Q_FAc = 0.098 (from Q_TFE = 0.032) and e_FAc = 1.23 (vs e_TFE = 1.63)], indicating that FAc is a strong electron‐withdrawing monomer as TFE. The normalized monomer‐diad and triad fractions as a function of the polymer composition were obtained from the comonomer sequence‐distribution procedure. The average molecular weights and molecular weight distributions as well as the thermal properties (glass‐transition temperature and decomposition temperature) of the fluorocopolymers were assessed and are discussed. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 1693–1706, 2004