Coordination polymer template synthesis of hierarchical MnCo2O4.5 and MnNi6O8 nanoparticles for electrochemical capacitors electrode

Two types of ternary metal oxides, MnCo₂O_4.5 and MnNi₆O₈ nanoparticles have been separately synthesized through chemical transformation from the corresponding bimetallic coordination polymer particles precursor under high-heating conditions. Series of electrochemical measurements are performed to examine the MnCo₂O_4.5 and MnNi₆O₈ electrodes, and the result shows that MnCo₂O_4.5 structure, especially for Mn/Co-600, has much higher capacitance than that of MnNi₆O₈ nanoparticles, indicating MnCo₂O_4.5 electrode is more suitable for applying in neutral electrolyte system. The Mn/Co-600 electrode exhibits a specific capacitance of 158 F g^?1 at 5 mV s^?1, good rate capability of 53.8% with a 20 times current density increase, good cycle performance (92.9% capacitance retention after 1000 cycles) and high power density (a specific power of 5760 W kg^?1 at 4.0 A g^?1) with low charge transfer resistance value of 1.8 Ω.