High-pressure synthesis, crystal structure and magnetic properties of a new cuprate (Nd,Ce)2+xCaCu2O6+y

New phase (Nd,Ce)_2+xCaCu₂O_6+y was prepared at a high-pressure/high-temperature condition of 6 GPa and 1300°C. It had a nonstoichiometric composition close to Nd_2.16Ce_0.225CaCu₂O_6+y. According to X-ray diffraction pattern, the Nd_2.16Ce_0.225CaCu₂O_6+y phase has a tetragonal lattice with a = 3.845(1) Å, c = 19.349(5) Å. However, electron microscopic observations revealed a complicated shear structure for this phase. Magnetic susceptibility and magnetic hysteresis measurements were performed for the Nd_2.16Ce_0.225CaCu₂O_6+y sample and it was found that the phase undergoes a weak ferromagnetic transition at 150 K. Below ≈40 K, complicated magnetic behavior was observed suggesting the presence of second weak ferromagnetic transition near 40 K.