熔融灰渣侵蚀耐火材料的界面特性研究
引用本文:徐荣声,林雄超,王永刚.熔融灰渣侵蚀耐火材料的界面特性研究[J].燃料化学学报,2015,43(2):138-144.
作者姓名:徐荣声  林雄超  王永刚
作者单位:School of Chemical and Environmental Engineering, China University of Mining and Technology (Beijing), Beijing 100083, China
基金项目:国家自然科学基金(21406261); 北京市优秀人才资助(2013D009014000001)。
摘    要:研究了碱酸比不同的3种熔融煤灰(A、J1和J2)在莫来石和刚玉两种耐火材料上的界面特性。结果表明,A对莫来石和刚玉都有很好的润湿性,而J1和J2对这两种耐火材料则经历由不完全润湿到润湿的过程。熔渣与耐火材料(S-R)界面宽度随着接触角减小而增大。从灰渣开始熔融至1 520 ℃,熔融煤灰J1在耐火材料表面上的接触角随着倾角的增加而减小;当倾角为20°时,其接触角突然增大。SEM-EDS分析表明,由于界面反应,A比J1更容易渗透进入耐火材料内部。对于碱酸比不同的煤灰,渗透和酸碱反应是熔渣对耐火材料腐蚀的关键。

关 键 词:耐火材料  灰渣  侵蚀  界面  
收稿时间:2014-10-14

Morphological and interfacial characterization of molten slags on the refractory surface
XU Rong-sheng,LIN Xiong-chao,WANG Yong-gang.Morphological and interfacial characterization of molten slags on the refractory surface[J].Journal of Fuel Chemistry and Technology,2015,43(2):138-144.
Authors:XU Rong-sheng  LIN Xiong-chao  WANG Yong-gang
Institution:School of Chemical and Environmental Engineering, China University of Mining and Technology (Beijing), Beijing 100083, China
Abstract:The interfacial properties between three types of coal slags (A, J1 and J2 with various base/acid ratio) and two refractory materials (mullite and corundum) were studied. The results indicate that the slag A has good wettability on both of refractory materials. While, the slags J1/J2 have experienced the process from incomplete wetting to whole wetting. The contact angles decrease with increasing of interface width of slag and refractory materials (S-R). The contact angles of J1 on mullite decrease with increasing of inclination angles from deformation temperature to 1 520 ℃, but significantly increase when the inclination angle is 20°. The SEM-EDS analysis show that the quantity of slag A permeating into the refractory material is more than that of J1 slags because of interfacial reaction. The infusion and acid-base reactions are the key factors for the refractory corrosion.
Keywords:refractory material  slag  erosion  interface