Au/TiO2/Ru(0 0 0 1) model catalysts and their interaction with CO

Au/TiO₂/Ru(0 0 0 1) model catalysts and their interaction with CO were investigated by scanning tunneling microscopy and different surface spectroscopies. Thin titanium oxide films were prepared by Ti deposition on Ru(0 0 0 1) in an O₂ atmosphere and subsequent annealing in O₂. By optimizing the conditions for deposition and post-treatment, smooth films were obtained either as fully oxidized TiO₂ or as partly reduced TiO_x, depending on the preparation conditions. CO adsorbed molecularly on both oxidized and reduced TiO₂, with slightly stronger bonding on the reduced films. Model catalyst surfaces were prepared by depositing submonolayer quantities of Au on the films and characterized by X-ray photoelectron spectroscopy and scanning tunneling microscopy. From X-ray photoelectron spectroscopy, a weak interaction between the Au and the TiO₂ substrate was found. At 100 K CO adsorption occurred on both the TiO₂ film and on the Au nanoparticles. CO desorbed from the Au particles with activation energies between 53 and 65 kJ/mol, depending on the Au coverage. If the Au deposit was annealed to 770 K prior to CO exposure, the CO adsorption energy decreased significantly. STM measurements revealed that the Au particles grow upon annealing, but are not encapsulated by TiO_x suboxides. The higher CO adsorption energy observed for smaller Au coverages and before annealing is attributed to a significantly stronger interaction of CO with mono- and bilayer Au islands, while for higher particles, the adsorption energy becomes more bulk-like. The implications of these effects on the known particle size effects in CO oxidation over supported Au/TiO₂ catalysts are discussed.