Epitaxial MoOx nanostructures on TiO2(1 1 0) obtained using thermal decomposition of Mo(CO)6

Stoichiometric and highly-defective TiO₂(1 1 0) surfaces (called as yellow and blue, respectively) were exposed to Mo(CO)₆ vapours in UHV and in a reactive O₂ atmosphere. In the case of yellow-TiO₂, an O₂ reactive atmosphere was necessary to obtain the Mo(CO)₆ decomposition at 450 °C with deposition of MoO_x nanostructures where, according to core level photoemission data, the Mo⁺⁴ state is predominant. In the case of blue-TiO₂ it was possible to obtain Mo deposition both in UHV and in an O₂ atmosphere. A high dose of Mo(CO)₆ in UHV on blue-TiO₂ allowed the deposition of a thick metallic Mo layer. An air treatment of this sample at 580 °C led to the elimination of Mo as MoO₃ and to the formation of a transformed layer of stoichiometry of Ti_(1−x)Mo_xO₂ (where x is close to 0.1) which, according to photoelectron diffraction data, can be described as a substitutional near-surface alloy, where Mo⁺⁴ ions are embedded into the titania lattice. This embedding procedure results in a stabilization of the Mo⁺⁴ ions, which are capable to survive to air exposure for a rather long period of time. After exposure of the blue-TiO₂(1 1 0) substrate to Mo(CO)₆ vapours at 450 °C in an O₂ atmosphere it was possible to obtain a MoO₂ epitaxial ultrathin layer, whose photoelectron diffraction data demonstrate that is pseudomorphic to the substrate.