Effect of heat treatment on the optical and electrical transport properties of Ge15Sb10Se75 and Ge25Sb10Se65 thin films

The effect of heat treatment on the optical and electrical properties of Ge₁₅Sb₁₀Se₇₅ and Ge₂₅Sb₁₀Se₆₅ thin films in the range of annealing temperature 373-723 K has been investigated. Analysis of the optical absorption data indicates that Tauc's relation for the allowed non-direct transition successfully describes the optical processes in these films. The optical band gap (E_g^opt.) as well as the activation energy for the electrical conduction (ΔE) increase with the increase of annealing temperature (T_a) up to the glass transition temperature (T_g). Then a remarkable decrease in both the E_g^opt. and ΔE values occurred with a further increase of the annealing temperature (T_a>T_g). The obtained results were explained in terms of the Mott and Davis model for amorphous materials and amorphous to crystalline structure transformations. Furthermore, the deduced value of E_g^opt. for the Ge₂₅Sb₁₀Se₆₅ thin film is higher than that observed for the Ge₁₅Sb₁₀Se₇₅ thin film. This behavior was discussed on the basis of the chemical ordered network model (CONM) and the average value for the overall mean bond energy 〈E〉 of the amorphous system Ge_xSb₁₀Se_90−x with x=15 and 25 at%. The annealing process at T_a>T_g results in the formation of some crystalline phases GeSe, GeSe₂ and Sb₂Se₃ as revealed in XRD patterns, which confirms our discussion of the obtained results.