Shift of Optical Absorption Edge in Sol-Gel Derived Transparent BaTiO3 Gels During Aging

Transparent barium titanate (BaTiO₃) wet gels synthesized by sol-gel processing using high-concentration Ba,Ti-alkoxide solution (1.0 mol/l) were subjected to optical measurements, X-ray diffraction analysis and transmission electron microscope observations. A systematic shift of the optical absorption edge was observed for the transparent BaTiO₃ wet gels shrinking during aging at 30 and 50°C, while no shift was observed for the wet gels aged at 5°C. The crystallinity and crystallite size of the gels increased with increasing aging time and temperature. The shift of the optical absorption edge of the BaTiO₃ gels during aging was found to have a close relation to an increase in the crystallite size of the gels.