Novel doubly polymerizable functional norbornene: Its synthesis,reactivity, and macromolecular architectures from a dual cure via ring‐opening metathesis polymerization and radical photopolymerization

A novel doubly polymerizable functional norbornene, 5‐(methacryloyloxyethylamino carboxylmethyl)bicyclo2.2.1]hept‐2‐ene (NBMOACM), was prepared. The ring‐opening metathesis polymerization (ROMP) of NBMOACM was carried out to prepare polymers with crosslinkable side chains with the Grubbs catalyst. No gel formation occurred during the ROMP of NBMOACM. The ¹H NMR spectrum of poly(NBMOACM) showed broad signals between 5.10 and 5.40 ppm, corresponding to the vinyl protons of the cis and trans double bonds of the ring‐opened polymer. Increasing the ratio of the monomer concentration to the catalyst concentration resulted in the formation of higher molecular weight polymers. Poly(NBMOACM) was incorporated into poly(methyl methacrylate) poly(MMA)] to produce AB crosslinked materials. These crosslinked materials 1 wt % poly(NBMOACM), 10% weight loss temperature = 300 °C in air] had higher thermal stability than pure poly(MMA) (10% weight loss temperature = 276 °C in air). © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6287–6298, 2006