Use of ESCA for a convenient and semi-quantitative state analysis of copper-nickel alloy surfaces

Summary A semi-quantitative technique by means of ESCA was applied to the surface state analysis of copper-nickel alloys. With area integrated intensity of peaks at the L₃M_{4, 5}M_{4, 5} region of copper and 2 p 3/2 region of nickel, cuprous state and nickel oxide state on alloys could be semi-quantitatively determined. As to oxygen states on alloy surfaces, interstitial (Cu₂O and NiO states), non-stoichiometric (represents -OH) and molecular states (adsorbed) were estimated. Further, the surface composition of alloys after heating under high vacuum was discussed.

---

Einsatz von ESCA für die einfache halbquantitative Zustandsanalyse von Oberflächen von Kupfer-Nickel-Legierungen

Zusammenfassung Das ESCA-Verfahren wurde für die Untersuchung des Oberflächenzustandes von KupferNickel-Legierungen eingesetzt. Mit Hilfe der flächenintegrierten Peakintensitäten (L₃ M_{4, 5} M_{4, 5} für Kupfer, 2 p 3/2 für Nickel) konnten Kupfer(II) und Nickeloxid auf den Legierungen halbquantitativ bestimmt werden. Sauerstoff wurde im interstitiellen (Cu₂O, NiO) nichtstöchiometrischen (-OH) und molekularen (adsorbierten) Zustand gefunden. Weiterhin wurde die Oberflächenzusammensetzung der Legierungen nach Erhitzen im Hochvakuum diskutiert.