Synthesis, characterization and thermal degradation mechanism of three poly(alkylene adipate)s: Comparative study

Three high molecular weight aliphatic polyesters derived from adipic acid and the appropriate diol - poly(ethylene adipate) (PEAd), poly(propylene adipate) (PPAd) and poly(butylene adipate) (PBAd) - were prepared by two-stage melt polycondensation method (esterification and polycondensation) in a glass batch reactor. Intrinsic viscosities, GPC, DSC, NMR and carboxylic end-group measurements were used for their characterization. Mechanical properties of the prepared polyesters showed that PPAd has similar tensile strength to low-density polyethylene while PEAd and PBAd are much higher. From TGA analysis it was found that PEAd and PPAd have lower thermal stability than poly(butylene adipate) (PBAd). The decomposition kinetic parameters of all polyesters were calculated while the activation energies were estimated using the Ozawa, Flynn and Wall (OFW) and Friedman methods. Thermal degradation of PEAd was found to be satisfactorily described by one mechanism, with activation energy 153 kJ/mol, while that of PPAd and PBAd by two mechanisms having different activation energies: the first corresponding to a small mass loss with activation energies 121 and 185 kJ/mol for PPAd and PBAd, respectively, while the second is attributed to the main decomposition mechanism, where substantial mass loss takes place, with activation energies 157 and 217 kJ/mol, respectively.