Study on permeation behavior and chemical degradation of PA66 in acid solution

In many polymers under corrosive liquids, degradation followed after permeation of environmental solution for a long period. The permeation rate of environmental solution, in many cases, is very low in corrosion-resistant polymeric materials. Therefore, the observation of the permeation of environmental solution and degradation of polymeric materials are very difficult in practical application. A simulation of permeation of solution is required in order to understand the permeation behavior of environmental solution and polymer degradation. A detailed analysis of the permeation behavior of solution accompanied by chemical reaction is important to study for improving the lifetime of polymers. Polyamide 66 (PA66) and sulfuric acid solution were used to investigate the quantitative study of permeation of environmental solution and its relation to degradation of polymeric materials. Correlation between diffusion process and degradation of PA66 related to the decrease of weight average molecular weight was defined. The diffusion rate of sulfuric acid solution was found to increase by decreasing weight average molecular weight of PA66 due to the established chain scission by hydrolysis reaction. The permeation of sulfuric acid solution that affected the decomposition reaction was modeled and quantitative evaluation of permeation of sulfuric acid was established.