Effect of Eu3+ concentration on microstructure and photoluminescence of Sr2SiO4:Eu3+ phosphors prepared by microwave assisted sintering

In this paper, effect of Eu³⁺ doping concentrations on microstructure and photoluminescence of Sr₂SiO₄ phosphors was investigated. The Sr_2?xSiO₄:xEu³⁺ phosphors with x=0.05, 0.1, 0.2, 0.3 were synthesized by microwave assisted sintering at 1200 °C for 60 min in air. X-ray powder diffraction analysis confirmed the formation of pure Sr₂SiO₄ phase without second phase or phases of starting materials irrespective of the adding amount of Eu³⁺. From scanning electron microscopy image, it is found that with more Eu³⁺ ions introduced to Sr₂SiO₄, the shape of the particles is not much different from each other, but the particle size decreases significantly from 1 to 2 μm (when x=0.05) to less than 500 nm (when x=0.3). The emission spectrum was located obviously at 617 nm as the excitation spectrum at λ_ex=395 nm, and it had best emission intensity when x=0.1.